RAL1014 ivory color pure polyester TGIC powder coating sprayed by electrostatic spray gun
polyester TGIC powder coatings will provide good edge cover when sharp edges are present, due to the inherent higher melt viscosities of TGIC-based coatings, which may also increase surface roughness (orange peel). Over-bake color stability of TGIC-based coatings is excellent.
Although adhesion and corrosion resistance properties are similar to polyester urethane coatings, chemical and solvent resistance may be somewhat reduced.
Application
Suitable for all kinds of products such as household appliances, instruments, meters medical devices,
automotive components, metal furniture, fitness equipment, indoor decorative painting, etc.
Also apply to a variety of equipment, pipes, pipe fittings and other requirements of corrosion coating.
Specification
| Inspection Item | Test Standard or Method
| Test Indicator |
| Type A | Type B,C |
| Impact resistance | ISO6272 | GB/T1732-1993 | 40cm | 50cm |
| Cupping test | ISO1520 | GB/T9753-1988 | 5mm | 8mm |
| Adhesion (Planning grid method) | ISO2409 | GB/T9286-1998 | Grade 0 |
| Crook | ISO1519 | GB/T6742-1986 | 3mm | 2mm |
| Pencil hardness | ASTMD3363 | GB/T6739-1996 | 1H-2H |
| Salt test | ISO7253 | GB/T1771-1991 | > 500 hours |
| Heat test | ISO6270 | GB/T1740-1979 | > 1000 hours |
| Heat resistance | 100°C/24 hours (white) | Paul Light character (best) |
| Remark | Spraying gun: Corona Coating Thickness: Minimum – 35 microns
Preferred – 55 microns
Maximum – 65 microns |
Powder physical properties:
Proportion : 1.2-1.8 (depending on the color and gloss ) .
Particle size distribution: 100% less than 125 microns (more than 85% between 60 to 90).
Liquidity(180°C):22~35mm.
Curing conditions:200°C,10 minutes.
Average coverage:
8-10m³/kg, the membrane is 60μm
(calculate by 100% utilization rate of powder coating).